316L rostfritt stål - Korrosionsbeständig

Tunga svetsapplikationer

In general, stainless steel is susceptible to intergranular corrosion due to the precipitation of chromium carbides between the grains during welding. It can also occur when carbon diffuses into the body of stainless steel from oil, plastic tape, and other organic substances under heat. The process is known as carburization. However, due to low carbon content, 316L thrives under such environments by offering excellent resistance to intergranular corrosion. Therefore, fabricators choose 316L over 316 in heavy gauge (>6 mm) svetsade komponenter.

 

Här är en kortfattad jämförelsetabell för 316L rostfritt stål med andra vanliga typer av rostfritt stål:

Typ av rostfritt stål	Korrosionsbeständighet	Draghållfasthet	Huvudsakliga kemiska komponenter	Typisk kostnad	Typiska applikationer
316L	Mycket hög	Hög	16-18% Cr, 10-14% Ni, 2-3% Mo,<0.03% C	Måttlig	Medicinsk utrustning, marina miljöer, kemisk bearbetning
304	Hög	Måttlig	18-20 % Cr, 8-12 % Ni,<0.08% C	Lägre	Köksutrustning, arkitektonisk panel
410	Måttlig	Hög	11,5-13,5 % Cr,<0.15% C	Lägre	Bestick, ånga och gasturbinblad
321	Hög	Hög	17-19% Cr, 9-12% Ni, 5x%C Ti	Högre	Flyg- och rymdkomponenter, avgassystem